Results of the summarizing process for the arXiv paper: 2104.11402v1

In this paper, the authors aimed to improve the wear resistance of components such as screws under severe friction-wear by developing Fe-Cr-C-Mo-V-Ti-N hardfacing coatings. These coatings were obtained using the shielded manual arc welding (SMAW) method. To enhance their properties, ferroalloys were added into the coating flux of the hardfaced electrode and jointly nitrided. The microstructure analysis of the coatings was conducted using various techniques including X-ray diffraction (XRD), optical microscope (OM), field emission scanning electron microscope (FESEM), and energy dispersive X-ray spectrometry (EDS). Additionally, FactSage 7.0 software was utilized to calculate the equilibrium phase diagram of the hardfacings. To evaluate their performance, wear resistance tests were performed on a pin-on-disc machine. The results showed that the Fe-Cr-C-Mo-V-Ti-N hardfacings exhibited higher wear resistance compared to cladding layers without nitrides. In terms of manufacturing process, five layers of hardfacing were deposited onto each steel substrate using SMAW method to ensure a homogeneous specimen. The welding parameters and total thickness of the layer were carefully controlled during deposition. Specimens with specific dimensions were cut from the longitudinal section of the weld layer and subjected to grinding and polishing processes for further analysis.

• - Authors aimed to improve wear resistance of components using Fe-Cr-C-Mo-V-Ti-N hardfacing coatings
• - Coatings obtained using shielded manual arc welding (SMAW) method
• - Ferroalloys added into coating flux and jointly nitrided to enhance properties
• - Microstructure analysis conducted using XRD, OM, FESEM, and EDS techniques
• - FactSage 7.0 software used to calculate equilibrium phase diagram of hardfacings
• - Wear resistance tests performed on pin-on-disc machine
• - Fe-Cr-C-Mo-V-Ti-N hardfacings showed higher wear resistance compared to cladding layers without nitrides
• - Five layers of hardfacing deposited onto each steel substrate using SMAW method for homogeneous specimen
• - Welding parameters and total thickness of layer carefully controlled during deposition
• - Specimens cut from longitudinal section of weld layer for further analysis after grinding and polishing processes.

The authors wanted to make things stronger by adding a special coating called Fe-Cr-C-Mo-V-Ti-N. They used a method called shielded manual arc welding to put the coating on. They also added something called ferroalloys to make the coating even better. They looked at the coating under a microscope using different techniques. They used a special software to figure out how the coating would work. They tested how well the coating could resist wear and found that it was better than other coatings without nitrides. They made sure each layer of the coating was the same and controlled how thick it was. Finally, they cut pieces from the coated material to study them more closely." Definitions - Wear resistance: How well something can withstand damage from rubbing or scraping. - Coatings: A layer of material that is put on top of something else to protect or improve it. - Shielded manual arc welding (SMAW): A method of joining two pieces of metal together using an electric current and a special rod. - Microstructure analysis: Studying what something looks like under a microscope to understand its properties. - Equilibrium phase diagram: A diagram that shows what different materials will look like when they are mixed together and cooled down. - Specimens: Small pieces taken from a larger object for testing or studying. - Homogeneous: When something is all the same throughout, with no differences in its parts.

Improving Wear Resistance of Components with Fe-Cr-C-Mo-V-Ti-N Hardfacing Coatings

In this research paper, the authors aimed to improve the wear resistance of components such as screws under severe friction and wear by developing Fe-Cr-C-Mo-V-Ti-N hardfacing coatings. These coatings were obtained using shielded manual arc welding (SMAW) method. To enhance their properties, ferroalloys were added into the coating flux of the hardfaced electrode and jointly nitrided.

Microstructure Analysis

The microstructure analysis of the coatings was conducted using various techniques including Xray diffraction (XRD), optical microscope (OM), field emission scanning electron microscope (FESEM), and energy dispersive Xray spectrometry (EDS). Additionally, FactSage 7.0 software was utilized to calculate the equilibrium phase diagram of the hardfacings.

Evaluating Performance

To evaluate their performance, wear resistance tests were performed on a pinon disc machine. The results showed that the FeCrCMoVTiN hardfacings exhibited higher wear resistance compared to cladding layers without nitrides.

Manufacturing Process

In terms of manufacturing process, five layers of hardfacing were deposited onto each steel substrate using SMAW method to ensure a homogeneous specimen. The welding parameters and total thickness of the layer were carefully controlled during deposition. Specimens with specific dimensions were cut from longitudinal section of weld layer and subjected to grinding and polishing processes for further analysis. Overall, it can be concluded that FeCrCMoVTiN hardfacings are an effective way to improve wear resistance in components subject to severe friction and wear conditions due to its superior properties compared to other cladding layers without nitrides.