The ever-increasing number of spent lithium-ion batteries (LIBs) has become a significant waste-management challenge. One important component of LIBs is the aluminium and copper current collectors, which make up more than 15% of the weight. Directly reusing these current collectors can effectively reduce LIB waste and provide a renewable source of aluminium and copper, while also avoiding lengthy manufacturing processes and associated energy input and material consumption. In this study, researchers successfully reclaimed aluminium and copper current collectors from commercial spent LIBs using different chemical treatments. These reclaimed current collectors were then reused for LiNi0.6Mn0.2Co0.2O2 cathodes and graphite anodes, respectively. The treated current collectors exhibited different surface compositions and morphology compared to pristine ones, resulting in distinct wettability, adhesion, and electrical conductivity properties. The reused current collectors demonstrated similar electrochemical performance to pristine ones at low C rates. However, caution should be exercised when using aluminium current collectors at high C rates due to their relatively low contact conductivity. This work provides substantial evidence that the direct reuse of aluminium and copper current collectors is possible. Additionally, the study highlights the importance of considering the surface morphology of current collectors during their reuse process. It was observed that a substantial amount of PVDF binder was located at the etched Al/NMC622 interface, indicating a high affinity between carbon black and PVDF binder in forming carbon binder domains (CBD). On the other hand, all three Cu current collectors showed similar adhesion forces with etched Cu exhibiting slightly higher adhesion forces compared to washed Cu and pristine Cu. Overall, this research contributes valuable insights into the direct reuse of aluminium and copper current collectors from spent LIBs by exploring different chemical treatments for reclamation as well as understanding how surface morphology affects performance characteristics such as wettability, adhesion, and electrical conductivity; thus providing a foundation for future efforts in sustainable battery waste management and resource recovery.

• - The increasing number of spent lithium-ion batteries (LIBs) is a waste-management challenge
• - Aluminium and copper current collectors make up over 15% of LIB weight
• - Directly reusing current collectors reduces waste and provides a renewable source of aluminium and copper
• - Researchers successfully reclaimed current collectors from commercial spent LIBs using chemical treatments
• - Reclaimed current collectors were reused for cathodes and anodes
• - Treated current collectors had different surface compositions and morphology compared to pristine ones, affecting properties like wettability, adhesion, and electrical conductivity
• - Reused current collectors showed similar electrochemical performance to pristine ones at low C rates but caution needed at high C rates for aluminium current collectors due to low contact conductivity
• - Surface morphology affects the reuse process, with observations of PVDF binder located at the etched Al/NMC622 interface and different adhesion forces for Cu current collectors

There are a lot of used batteries that we need to figure out what to do with. Some parts of the batteries, called current collectors, are made of aluminum and copper and they make up a big part of the battery's weight. Instead of throwing away these current collectors, scientists found a way to use them again. They treated the used current collectors with chemicals and then used them in new batteries. The treated current collectors looked different than new ones and this affected how well they worked in the new batteries. So, we need to be careful when using them in certain situations." Definitions- Lithium-ion batteries (LIBs): Batteries that use lithium ions to store and release energy. - Waste-management: The process of handling and disposing waste materials. - Aluminium: A lightweight metal often used in making things like cans or foil. - Copper: A reddish-brown metal that is a good conductor of electricity. - Reusing: Using something again instead of throwing it away. - Renewable source: Something that can be replaced or replenished naturally over time. - Chemical treatments: Using chemicals to change or clean something. - Cathodes and anodes: Parts of a battery where electric currents flow in and out. - Pristine: In perfect condition or untouched by anything harmful. - Wettability: How easily something can be wetted by a liquid (like water). - Adhesion: How well two things stick together. - Electrical conductivity: How easily electricity can pass through something.

Reusing Aluminium and Copper Current Collectors from Spent Lithium-Ion Batteries

The ever-increasing number of spent lithium-ion batteries (LIBs) has become a significant waste-management challenge. One important component of LIBs is the aluminium and copper current collectors, which make up more than 15% of the weight. Directly reusing these current collectors can effectively reduce LIB waste and provide a renewable source of aluminium and copper, while also avoiding lengthy manufacturing processes and associated energy input and material consumption. In this study, researchers successfully reclaimed aluminium and copper current collectors from commercial spent LIBs using different chemical treatments.

Chemical Treatments for Reclamation

The research team used three different chemical treatments to reclaim the current collectors: etching with hydrochloric acid (HCl), washing with deionized water, or no treatment at all (pristine). These reclaimed current collectors were then reused for LiNi0.6Mn0.2Co0.2O2 cathodes and graphite anodes, respectively. The treated current collectors exhibited different surface compositions and morphology compared to pristine ones, resulting in distinct wettability, adhesion, and electrical conductivity properties.

Electrochemical Performance

The reused current collectors demonstrated similar electrochemical performance to pristine ones at low C rates; however caution should be exercised when using aluminium current collectors at high C rates due to their relatively low contact conductivity. It was observed that a substantial amount of PVDF binder was located at the etched Al/NMC622 interface indicating a high affinity between carbon black and PVDF binder in forming carbon binder domains (CBD). On the other hand all three Cu current collector showed similar adhesion forces with etched Cu exhibiting slightly higher adhesion forces compared to washed Cu & pristine Cu .

Conclusion

This work provides substantial evidence that the direct reuse of aluminium & copper current collector is possible & highlights importance of considering surface morphology during their reuse process . Overall this research contributes valuable insights into direct reuse of aluminum & copper from spent LIBs by exploring different chemical treatments for reclamation as well as understanding how surface morphology affects performance characteristics such as wettability ,adhesion & electrical conductivity ; thus providing foundation for future efforts in sustainable battery waste management & resource recovery .