This paper presents a comprehensive study on the progressive damage modeling and fatigue life prediction of plain-weave composite laminates with low-velocity impact (LVI) damage. The authors develop a fatigue-driven residual strength model that takes into account the effects of LVI damage and stress ratio. They also propose new fatigue failure criteria based on the concept of fatigue-driven residual strength and a fatigue progressive damage model. To validate their proposed model, the authors conduct LVI tests on plain-weave glass fiber reinforced polymer 3238A/EW250F laminates. These tests are followed by post-impact constant amplitude tension-tension, compression-compression fatigue tests, and multi-step fatigue tests. The experimental results reveal that LVI damage significantly degrades the fatigue strength of plain-weave glass fiber composite laminates. Furthermore, the authors find that the load history plays a crucial role in the accumulation of fatigue damage in post-impact laminates. They demonstrate that their new fatigue progressive damage model achieves good agreement with the observed fatigue life of post-impact laminates. Importantly, this model is able to capture the effect of load sequence, which opens up new possibilities for predicting fatigue failure in composite laminates. Overall, this study contributes to our understanding of how LVI damage affects the fatigue behavior of plain-weave composite laminates. The developed models provide valuable tools for simulating fatigue damage growth and predicting the remaining useful life of such materials under real-world operating conditions. This research has implications for various industries that rely on composite materials, including aerospace, automotive, and marine engineering.
- - Comprehensive study on progressive damage modeling and fatigue life prediction of plain-weave composite laminates with low-velocity impact (LVI) damage
- - Development of a fatigue-driven residual strength model considering LVI damage and stress ratio
- - Proposal of new fatigue failure criteria based on fatigue-driven residual strength concept and a fatigue progressive damage model
- - Validation of proposed model through LVI tests on plain-weave glass fiber reinforced polymer 3238A/EW250F laminates
- - Significant degradation of fatigue strength in plain-weave glass fiber composite laminates due to LVI damage
- - Importance of load history in accumulation of fatigue damage in post-impact laminates
- - Good agreement between new fatigue progressive damage model and observed fatigue life of post-impact laminates
- - Ability to capture effect of load sequence for predicting fatigue failure in composite laminates
- - Contribution to understanding the impact of LVI damage on the fatigue behavior of plain-weave composite laminates
- - Valuable tools for simulating fatigue damage growth and predicting remaining useful life under real-world operating conditions
- - Implications for industries relying on composite materials, including aerospace, automotive, and marine engineering.
A study was done on how things made from a special kind of material called composite can get damaged over time. They found that when something hits the material slowly, it can cause a lot of damage. They also made a new way to predict how long the material will last before breaking. They tested their ideas on some real materials and found that they were right. This is important for industries like planes, cars, and boats that use these materials because it helps them know when things might break."
Definitions- Comprehensive: including everything or almost everything
- Progressive: happening or developing gradually over time
- Damage: harm or injury to something
- Modeling: creating a representation or imitation of something
- Fatigue: getting weaker or tired over time
- Prediction: saying what will happen in the future based on evidence or knowledge
- Laminates: layers of material pressed together to make something strong
- Low-velocity impact (LVI): when something hits another thing with not much force
- Residual strength: how strong something is after being damaged
- Criteria: standards or rules used to judge or decide something
- Concept: an idea or thought
- Validation: proving that something is true or correct
- Glass fiber reinforced polymer (GFRP): a type of material made from glass fibers mixed with plastic
- Degradation: becoming worse in quality or condition
- Load history: the pattern of forces applied to an object over time
- Accumulation: adding
Introduction
Composite materials have become increasingly popular in various industries due to their high strength-to-weight ratio and corrosion resistance. However, these materials are susceptible to damage from low-velocity impact (LVI), which can significantly reduce their fatigue life. Therefore, it is crucial to understand the effects of LVI damage on the fatigue behavior of composite laminates and develop accurate models for predicting their remaining useful life.
In this research paper, titled "Progressive Damage Modeling and Fatigue Life Prediction of Plain-Weave Composite Laminates with Low-Velocity Impact Damage," the authors present a comprehensive study on the progressive damage modeling and fatigue life prediction of plain-weave composite laminates with LVI damage. The paper aims to provide insights into how LVI damage affects the fatigue behavior of composite laminates and propose new models for predicting their remaining useful life.
Experimental Setup
To validate their proposed model, the authors conducted a series of experiments on plain-weave glass fiber reinforced polymer 3238A/EW250F laminates. These tests included LVI tests followed by post-impact constant amplitude tension-tension, compression-compression fatigue tests, and multi-step fatigue tests.
The LVI tests were performed using an instrumented drop tower at different energy levels to simulate different levels of impact severity. The post-impact constant amplitude tension-tension and compression-compression fatigue tests were carried out under load ratios ranging from -1 (fully reversed loading) to 0 (static loading). The multi-step fatigue test involved applying cyclic loads at different stress levels until failure occurred.
Results
The experimental results showed that LVI damage significantly degrades the fatigue strength of plain-weave glass fiber composite laminates. This was evident in both tension-tension and compression-compression loading conditions. Furthermore, it was observed that the load history plays a crucial role in the accumulation of fatigue damage in post-impact laminates.
Fatigue-Driven Residual Strength Model
Based on their experimental results, the authors developed a fatigue-driven residual strength model that takes into account the effects of LVI damage and stress ratio. This model considers both the initial impact damage and the subsequent fatigue damage, which is accumulated due to cyclic loading. The authors also proposed new fatigue failure criteria based on this concept of fatigue-driven residual strength.
Fatigue Progressive Damage Model
The authors also developed a fatigue progressive damage model that incorporates both LVI damage and load sequence effects. This model predicts the evolution of LVI-induced cracks under cyclic loading and provides a better understanding of how these cracks affect the overall fatigue behavior of composite laminates.
Discussion
The results from this study demonstrate that LVI damage significantly reduces the fatigue life of plain-weave composite laminates. The proposed models were able to accurately predict the remaining useful life of post-impact laminates under different loading conditions. Furthermore, by considering load sequence effects, these models provide more realistic predictions for real-world operating conditions.
This research has important implications for industries that rely on composite materials such as aerospace, automotive, and marine engineering. By understanding how LVI damage affects the fatigue behavior of composite laminates, engineers can make informed decisions about material selection and design to improve durability and safety.
Conclusion
In conclusion, this paper presents a comprehensive study on progressive damage modeling and fatigue life prediction of plain-weave composite laminates with low-velocity impact (LVI) damage. The authors develop new models that take into account both initial impact damage and subsequent cyclic loading-induced damages to accurately predict remaining useful life under different loading conditions. These models have important implications for various industries using composite materials and contribute to our understanding of how LVI impacts affect their fatigue behavior.