Results of the summarizing process for the arXiv paper: 2007.01937v1

This study examines the degradation of lithium-ion battery cells from three different manufacturers (Sony, BYD, and Samsung) and evaluates their performance in powering electric vehicles and integrating grid-connected renewable energy resources. The battery cells analyzed include Sony and BYD cells with LFP chemistry, as well as a Samsung cell with NMC chemistry. The researchers conducted extensive experiments to measure the capacity fade and resistance increase of the battery cells due to calendar aging and cycle aging. They identified several key parameters that affect calendar aging, including charge level and temperature. For cycle aging, the depth of discharge, current rate, and temperature were found to be significant factors. The results showed that after 30 months of use, the Sony LFP cells experienced a calendar capacity loss of approximately 5%, while the BYD LFP cells had a loss of around 8%. In comparison, the Samsung NMC cell demonstrated better cycle life, reaching an 80% state of health after 3000 cycles at a temperature of 35°C and a discharge depth of 75%. These findings provide valuable insights into the degradation behavior of lithium-ion battery cells from different manufacturers. By understanding how these batteries degrade over time under various conditions, researchers can develop strategies to improve their lifespan and enhance their economic viability for electric vehicle applications and grid integration of renewable energy resources.

• - Study examines degradation of lithium-ion battery cells from Sony, BYD, and Samsung
• - Evaluates performance in powering electric vehicles and integrating grid-connected renewable energy resources
• - Battery cells analyzed include Sony and BYD cells with LFP chemistry, as well as a Samsung cell with NMC chemistry
• - Extensive experiments conducted to measure capacity fade and resistance increase due to calendar aging and cycle aging
• - Key parameters affecting calendar aging identified: charge level and temperature
• - Significant factors for cycle aging found to be depth of discharge, current rate, and temperature
• - After 30 months of use, Sony LFP cells experienced approximately 5% calendar capacity loss, BYD LFP cells had around 8% loss
• - Samsung NMC cell demonstrated better cycle life, reaching 80% state of health after 3000 cycles at a temperature of 35°C and a discharge depth of 75%
• - Findings provide insights into degradation behavior of lithium-ion battery cells from different manufacturers
• - Understanding degradation over time can help develop strategies to improve lifespan and economic viability for electric vehicle applications and grid integration of renewable energy resources.

A study looked at how well batteries from Sony, BYD, and Samsung work in electric vehicles and with renewable energy. They tested different types of battery cells and did many experiments to see how they change over time. They found that the level of charge and temperature affect how long the batteries last. The Sony batteries lost about 5% of their capacity after 30 months, while the BYD batteries lost about 8%. The Samsung batteries lasted longer, even after being used 3000 times at a high temperature." Definitions- Degradation: When something gets worse or breaks down over time. - Lithium-ion battery cells: A type of rechargeable battery used in many electronic devices. - Performance: How well something works or performs its job. - Powering: Giving energy or electricity to make something work. - Electric vehicles: Cars or other vehicles that run on electricity instead of gasoline. - Integrating: Combining or putting together different things to work together. - Grid-connected renewable energy resources: Using sources like wind or solar power to generate electricity that can be connected to an electrical grid system. - Chemistry: The type or composition of a substance. - Experiments: Tests done to learn more about something by trying different things and seeing what happens. - Capacity fade: When a battery loses some of its ability to hold a charge over time. - Resistance increase: When it becomes harder for electricity to flow through a battery as it gets older. - Calendar aging: How a

Understanding the Degradation of Lithium-Ion Battery Cells for Electric Vehicle and Grid Integration Applications

The use of lithium-ion batteries to power electric vehicles (EVs) and integrate grid-connected renewable energy resources is becoming increasingly popular. However, one major challenge with these batteries is their degradation over time due to calendar aging and cycle aging. To better understand this phenomenon, researchers from the University of California San Diego conducted an extensive study on battery cells from three different manufacturers – Sony, BYD, and Samsung – to evaluate their performance in EV applications and grid integration. This article will discuss the findings of this research paper in detail.

Calendar Aging

The researchers first examined how calendar aging affects the capacity fade and resistance increase of lithium-ion battery cells. To do so, they tested a variety of parameters including charge level, temperature, depth of discharge (DoD), current rate, etc., for each cell type. The results showed that after 30 months of use, the Sony LFP cells experienced a calendar capacity loss of approximately 5%, while the BYD LFP cells had a loss of around 8%.

Cycle Aging

Next, they evaluated cycle aging by measuring how many cycles each cell could withstand before reaching an 80% state of health (SOH). They found that among all three types tested – Sony LFP cells, BYD LFP cells and Samsung NMC cell – it was the latter that demonstrated better cycle life when subjected to various conditions such as temperature (35°C) and DoD (75%). After 3000 cycles at these settings, it reached an SOH level close to 80%.

Conclusion

Overall, this research provides valuable insights into the degradation behavior of lithium-ion battery cells from different manufacturers. By understanding how these batteries degrade over time under various conditions such as charge level or temperature during calendar aging or DoD during cycle aging , researchers can develop strategies to improve their lifespan and enhance their economic viability for electric vehicle applications and grid integration of renewable energy resources.